{"id":3418,"date":"2011-07-07T14:50:55","date_gmt":"2011-07-07T14:50:55","guid":{"rendered":"https:\/\/mtlsites.mit.edu\/annual_reports\/2011\/?p=3418"},"modified":"2011-07-19T20:31:26","modified_gmt":"2011-07-19T20:31:26","slug":"cnt-based-optoelectronic-device-packaging-2","status":"publish","type":"post","link":"https:\/\/mtlsites.mit.edu\/annual_reports\/2011\/cnt-based-optoelectronic-device-packaging-2\/","title":{"rendered":"CNT-based Optoelectronic Device Packaging"},"content":{"rendered":"

Carbon nanotubes (CNTs) are excellent heat spreaders for packaging electronic\/photonic devices due to their high thermal conductivity and good mechanical strength [1<\/a>] <\/sup> [2<\/a>] <\/sup>. They have been used for packaging LED chips [3<\/a>] <\/sup> [4<\/a>] <\/sup> [5<\/a>] <\/sup>. However, poor adhesion between CNTs and adjacent materials may impact device yield and reliability. We proposed a platform for optoelectronic device packaging by integrating vertical aligned CNTs (VACNTs) onto patterned silicon U-grooves for achieving enhanced thermal conduction and stable mechanical properties.<\/p>\n

Figure 1 shows the schematic of the CNT-based platform. CNTs are grown on a silicon trench to provide heat spreading for the bonded device chip. A thin dielectric layer between CNTs and silicon substrate is usually needed to eliminate current leakage to the substrate. The device chip is bonded to the platform by the bonding pads on chip surface. Figure 2 shows the calculated thermal resistance of the CNT platform by using the Finite Element Method. A silicon monoxide (SiO) film of 500-nm thick is used as the dielectric layer. The planar silicon platform with the same thickness of SiO is also simulated for comparisons. When the top open area of the U-groove covers about 87% of the device chip and the depth is about 30% of the 200-mm thick silicon substrate, the CNT platform can provide about 39% reduction in thermal resistance if the thermal conductivity of CNTs is 600 W\/mK. The reduction can reach about 50% by using a deeper U-groove with taller CNTs. The enhancement on the thermal conduction by the CNT platform results not only from the use of high-thermal-conductivity VACNTs but also from the increased surface area of the low-thermal-conductance dielectric layer.<\/p>\n

The CNT platforms were demonstrated for packaging red LEDs to have high saturation current and high manufacturing yield [6<\/a>] <\/sup>.<\/p>\n\n\t\t