{"id":3315,"date":"2011-07-11T17:43:09","date_gmt":"2011-07-11T17:43:09","guid":{"rendered":"https:\/\/mtlsites.mit.edu\/annual_reports\/2011\/?p=3315"},"modified":"2011-07-19T20:27:14","modified_gmt":"2011-07-19T20:27:14","slug":"high-speed-graphene-circuits-and-photodetectors-2","status":"publish","type":"post","link":"https:\/\/mtlsites.mit.edu\/annual_reports\/2011\/high-speed-graphene-circuits-and-photodetectors-2\/","title":{"rendered":"High-speed Graphene Circuits and Photodetectors"},"content":{"rendered":"

The most common substrate for processing chemical vapor deposition (CVD) graphene and highly oriented pyrolytic graphite (HOPG) has been thermally grown silicon dioxide on top of silicon. Due to optical interference, monolayer and bilayers of graphene can be easily identified using a standard optical microscope [1<\/a>] <\/sup>. Furthermore, graphene is capacitively coupled to the underlying silicon, allowing for rapid electrical characterization through substrate biasing. While this substrate has proven useful for probing carrier transport in graphene as well as for developing graphene processing technology, the parasitic capacitances associated with the underlying silicon limit high-frequency performance. In this work, we have explored fabrication of graphene on purely insulating substrates, specifically sapphire. Sapphire is a common substrate used for radio frequency (RF) applications due to its low conductivity. Furthermore, it is much cheaper than other insulating substrates such as SiC or diamond.<\/p>\n

Through recent advances in improved ohmic processing using an oxidized aluminum capping layer, we are able to fabricate high-speed field effect transistors on both silicon dioxide and sapphire [2<\/a>] <\/sup>. Figure 1 shows measured RF data for a device with gate length (Lg<\/sub>) = 2 \u00b5m and width (W) = 25 \u00b5m on each substrate. While RF performance of graphene on silicon is slightly better after de-embedding than that of the sample on sapphire, we attribute this discrepancy to non-optimized processing conditions, possibly due to the transfer anneal or fabrication problems on transparent substrates. Fortunately, we are still able to achieve an extrinsic ft<\/sub>-Lg<\/sub> product of 14 GHz-\u00b5m on sapphire, which to our best knowledge is the highest reported extrinsic value on CVD graphene (Figure 2 [3<\/a>] <\/sup> [4<\/a>] <\/sup> [5<\/a>] <\/sup> [6<\/a>] <\/sup> [7<\/a>] <\/sup> [8<\/a>] <\/sup> ). In parallel, scanning photocurrent measurements of graphene on silicon dioxide show optical sensitivities of 0.4 mA\/W for large-area devices (>375 \u00b5m2<\/sup>). Therefore, combining our results on sapphire with optical measurements should hopefully allow for large-area arrays of high-speed graphene photodetectors.<\/p>\n\n\t\t